完全熔融状态下SiO2-Al2O3-CaO体系的黏度分析与预测 |
|
|
张志文 王增莹 梁钦锋 郭庆华 于广锁 于遵宏 |
|
|
煤气化教育部重点实验(华东理工大学) 煤气化教育部重点实验(华东理工大学) 煤气化教育部重点实验(华东理工大学) 煤气化教育部重点实验(华东理工大学) 煤气化教育部重点实验(华东理工大学) 煤气化教育部重点实验(华东理工大学) |
|
|
摘要：
基于网状结构模型概念，简要分析了SiO2-Al2O3-CaO体系各组分在网状结构中的作用。网状结构模型理论认为Al2O3为两性物，Al3+易形成四配位，部分电荷由具有较低场强的碱金属或碱土金属离子补偿。为考察SiO2-Al2O3-CaO体系随n(CaO)/[n(CaO)+n(Al2O3)]比值变化的黏度特性，研究了n(CaO)/[n(CaO)+n(Al2O3)]比值在0.4~0.6附近的黏温曲线变化规律。结果表明，硅熔体黏度随n(CaO)/ [n(CaO)+n(Al2O3)]比值的增大呈现先缓慢升高后降低的趋势，但当n(CaO)/[n(CaO)+n(Al2O3)]比值为0.5时，其黏度并非为最大值。基于流体流动特性，提出了SiO2-Al2O3-CaO体系在完全熔融状态下的黏度预测模型，并同传统的Urbain模型进行比较。结果表明，本模型预测效果好于Urbain模型，预测值同实验值更为接近。 |
|
|
关键词：
黏度
硅熔融体
煤气化
|
|
|
Analysis and Prediction of the Viscosity of the SiO2-Al2O3-CaO Ternary System in Completely Molten State |
|
|
ZHANG Zhi-wen WANG Zeng-ying LIANG Qin-feng GUO Qing-hua YU Guang-suo YU Zun-hong |
|
|
|
|
|
Abstract:
Based on the theory of random network model, the effects on the structure role in the SiO2-Al2O3-CaO ternary system for each component was analysed. The theory of random network model considers the amphoteric role of Al2O3 in the silicate system, and its strong preference for tetrahedral coordination with its charge deficit being compensated by alkaline earth metal cations, Mn+ etc. For studying the varied viscosity with the ratio of n(CaO)/[n(CaO)+n(Al2O3)] in the SiO2-Al2O3-CaO ternary system, the relationship between viscosity and component with the ratio of that typically in the range of 0.4~0.6 was investigated. The results show that, with the ratio of n(CaO)/[n(CaO)+n(Al2O3)] increasing from 0.4~0.6, the viscosity of the silicate melts increases slowly at first, and then decreases fiercely, but when that was at 0.5, the viscosity of silicate melts never reaches the maximum. Ground on the properties of fluid, the mathematical model for SiO2-Al2O3-CaO ternary system in completely molten state was established, which was better than the conventional Urbain model, and good agreement between experimental value and prediction one was obtained. |
|
|
Keywords:
viscosity
silicate melts
coal gasification
|
|
|
收稿日期 2007-06-25 修回日期 1900-01-01 网络版发布日期 |
|
|
DOI: |
|
|
基金项目:
|
|
|
通讯作者: 张志文 |
|
|
作者简介: |
|
作者Email: comingtozzw@163.com |
|
|
| 参考文献： |
|
| 本刊中的类似文章 |
| 1．廖瑞金 梁帅伟 李剑 郝建 尹建国.矿物油和天然酯混合绝缘油的
理化特性和击穿电压研究
[J]. 中国电机工程学报, 2009,29(13): 117-123 |
| 2．张海军 祝长生 杨琴.有效黏度效应对气体径向微轴承性能的影响[J]. 中国电机工程学报, 2009,29(29): 84-88 |
| 3．张邵波 骆仲泱 寿春晖 倪明江 岑可法.层流区CuO–水纳米流体流动与对流换热特性[J]. 中国电机工程学报, 2009,29(32): 58-65 |
|
| Copyright by 中国电机工程学报 |